SF 6 1.6 CF B-B 1000 KG

SF 6 1.6 CF B-B 1000 KG

Characteristics:


- Dry silica mass based on high purity microcrystalline quartzite.


- Mixed with a special sintering agent that gives it higher refractoriness.


- Bigger resistance against erosion, penetration and wetting of melting metal.


 


Application:


Lining of high, medium and low frequency coreless induction furnaces melting spheroidal iron, alloyed iron with high temperature casting, alloyed steel castings, and generally, any cast iron demanding better performance qualities than CUARSIL IS6 with Boron Oxide or Boric Acid.

Inicie sesión o regístrese para ver el precio y comprar

  • Ficha técnica Insertec
    Condiciones de Humedad It is guaranteed a maximum of 0.2 % of moisture at the end of the manufacturing process. When the material is going to be used, moisture content must be checked as it can change depending on the transport, storing or environmental conditions.
    Caracteristicas Dry silica mass based on high purity microcrystalline quartzite, mixed with a special sintering agent that gives it higher refractoriness, bigger resistance against erosion, penetration and wetting of melting metal.
    Aplicacion Lining of high, medium and low frequency coreless induction furnaces melting spheroidal iron, alloyed iron with high temperature casting, alloyed steel castings, and generally, any cast iron demanding better performance qualities than CUARSIL IS6 with Bor
    temperatura 1700ºC
    Granulometria 0-6 mm
    Tipo de Ligante Chemical – Ceramic.
    Analisis Quimico Al2O3 - Max.0,9%, SiO2 - (95-98)%; Fe2O3 - Máx.0,4%
    Densidad >2.160 kg/m3
    Instalacion Dry hand ramming or using specific vibration equipments for bottom and sidewalls. See instructions manual.
    Almacenamiento Pallets must be stored in a dry place. Once open, it must be totally consumed or, at least, cover the remaining sacks with a plastic sheet. Maximum lifetime: 12 months.
    Embalaje Big-Bag 1000 kg
    Calentamiento y Sinterizado Calentar hasta la Tª de trabajo a razón de 100-180ºC/H en función de la capacidad del horno.
    Agua necesaria colar / vibrar Depending on furnace’s capacity, heat up to working temperature at a rate of 100-180ºC/h. Sintering should be done at 30-50ºC over the working temperature, keeping this temperature during 0.5-2 hours. See instructions manual.